Dia 4m Cement Castings Mill Lining System With HRC50 Hardness And AK50J DF090

DF090

Send Inquiry

Description

Dia 4m Cement Castings Mill Lining System With HRC50 Hardness And AK50J DF090?

? Quick Details
1. Better surface quality for cement mill liners;
2. High hardness: more than HRC50;
3. Higher impact value: more than 50J.
?
Dia 4m Cement Mill Liner Castings?Description:
The?cast liners for cement mills?have the following features:
1.?Hardness: more than HRC50;
2. Impact Value: more than 50J;
3. Special heat-treatment process: Aiming at Cr-Mo alloy steel castings with higher hardness & higher impact value & even hardness distribution, we design a special quenching process, called Double-media quenching technique with water-based quenching liquid.
4. Internal Quality: we check the internal quality with UT test;
5. External Quality: we check the external quality with MT test & visual inspection;
6.? Package: Packed by steel pallets.
7. We supplied the cement mill liners to Shanghai Heavy Machinery Plant & Conch Cement Group.
?
?

In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
?
?

- - - -
Item | Cr-Mo
Alloy Steel I | Cr-Mo
Alloy Steel II | Cr-Mo
Alloy Steel III | High Cr white iron | High Cr Alloy Steel | High Manganese Steel | Ni-Hard cast iron |
C | 0.30~0.50 | 0.65~0.90 | 0.40~0.90 | 2.40~3.20 | 1.1~2.2 | 0.90~1.30 | 2.40~3.60 |
Si | 0.50~1.20 | ≤0.75 | 0.70~1.20 | 0.60~1.20 | 0.60~1.20 | ≤0.08 | ≤0.80 |
Mn | 0.40~1.20 | 0.50~1.20 | 0.60~1.00 | 0.50~1.00 | 0.50~1.00 | 11.00~18.00 | ≤2.0 |
Cr | 1.70~2.50 | 1.50~2.50 | 4.00~7.00 | 12.00~30.00 | 11.00~30.00 | 1.50~2.50 | 1.5~10 |
S | ≤0.04 | ≤0.06 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
P | ≤0.04 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
Mo | ≤0.5 | ≤0.5 | ≤0.5 | 0.10~3.0 | 0.10~3.0 | ≤1.0 | ≤0.10 |
Cu | 0.10~0.60 | ≤0.25 | 0.20~0.40 | 0.10~1.00 | 0.10~1.00 | - | - |
Ni | ≤0.50 | ≤0.30 | 0~0.30 | 0~0.30 | 0~0.30 | - | 3.3~10 |
Re | ≤0.02 | ≤0.02 | ≤0.02 | - | - | - | - |
Equivalent
Specifications | DL/T 681-1999
?
GB/T26651-2011 | AS 2074 L2B Mod | DL/T 681-1999 | GB/T 8263-1999
AS 2027 Cr27
AS 2027 CrMo 15/3
AS 2027 CrMo 20/2/1
ASTM A532 Class III type A 25% Cr
ASTM A532Class II type B 15% Cr-Mo
BS 4844 3E
DIN1695
NFA32401. | GB/T 5680-1998
DL/T 681-1999
JIS G 5153-1999
ASTM A 128
DIN GX120Mn12
AFNOR:Z120Mn12 | GB/T 8263-1999
AS 2027/Ni-Cr1-550
AS 2027/Ni-Cr2-500
AS 2027/Ni-Cr4-500
AS 2027/Ni-Cr4-600
AS 2027/Ni-Cr4-630
ASTM A 532 1-A,B,C,D
ASTM A 532 2-A,B,C,D,E
ASTM A 532 3-A |
Material Type | Martensite Steel | Martensite or
Pearlitic Cr Mo Steel | Martensite Steel | Martensite matrix | Austenitic Mn Steel | - |
Hardness | HRc≥48 | HB470 &
HB 321~370 | HRc≥50 | HRc≥56 | HB≤300 | HRc≥56 |
Impact Value | Ak≥40J | - | Ak≥10J | Ak≥4J | Ak≥80J | - |
- - - -

?
?

?

Read More